High-end PVC Coated Film designed for financial bank card lamination
High-end PVC Coated Film designed for financial bank card lamination is speically designed for high-end card lamination including financial bank cards. It has very good lamination performance inclduing stronger adhesion level, longer aging life and less color change or shrinkage ration after lamination.
PVC Strong Coated Overlay Film with Strong initial viscous force, slow decline , yellowing resistance ,
deformating resistance after laminating .The surface is smooth and easy to use. Mainly used for protective
film of bank card , social security card , IC card , RF card and other card with higher requirements .
PVC Coated Overlay MCO-W model is suitable for laminating with most PVC sheets printed by various printers . It features high adhesion , no color change and deformation .
It is applicable to almost all sheets printed by various ink . It features excellent peeling strength and long aging time .
| Item | Parameters |
| Vicat softening point | 72±2 ℃ |
| Heating Shrinkage ratio | ≤ 10 % |
| Tensile Strength | ≥ 40 MPa |
| Normal thickness in mm | 0.04 , 0.05,0.06,0.08,0.10 |
| Peel Strength (90°, 300mm/min) | ≥ 6.0 N/cm |
| Aging time (65℃ temp./95% humidity ) | ＞200 hours |
| Suitable ink | offset and silk screen printing UV ink, Pigment and dye ink for inkjet printing as well as digital printing ink |
1. Size : in reel or sheet , A4 , A3 or as per customer requirements
2. Normal thickness : 0.04,0.05,0.06,0.08,0.10mm
3. Color : transparent with one-side glue coating
4. Package method : by reel or 500 sheets per bag / 4-8 bags per paper carton , or as per customer requirements
5. Storage condition: Sealed , moisture-proof , room temperature under 40℃ , Keep it horizontally, avoid heavy pressing and direct sunlight .