PETG Plastic Sheet /PETG Card Core sheet for Smart Cards and high-end credit cards Production
1. PETG Plastic Sheet /PETG Card Core sheet for high-end credit cards and Smart cards Production- Introduction
PETG (Polyethylene Terephthalate) card core sheet is widely used in card base production. It has such features as impact resistance, high temperature resistance, anti-static, abrasion, folding and high strength. It is widely used for the production of high-end credit cards, ID cards and passport, etc.
PETG is a kind of transparent amorphous copolyester.
Features:
1).Excellent strength and wear-resisting
2).High temperature and low temperate resistance;
3).Perfect application for laser Engraving
4).Environment-friendly material
5).Longer service life
| Item | PETG Core Sheet |
| Color | White |
| Thickness Range(mm) | 0.1-0.76 |
| Vicat point ℃ | 78-80 ± 2 |
| Tensile strength | ≥50 Mpa |
| Surface | Both sides matt |
| Density | 1.3 ± 0.05 |
| Transparency | ≤5 |
| Heat shrink | ≥-8.0 % (longitudinal) &≥-4.0 %(transverse) |
2.PETG Plastic Sheet /PETG Card Core sheet for high-end credit cards and Smart cards Production- Parameters
It is used for national ID cards and other high grade cards.It is capable of achieving laser ablation, sunken cord, leveling up, printed layer,and has resistance to high temperature, high strength and environmental protection.
Technical Parameters:
| Item | Parameters |
| Vicat softening point (B50) | 78±2 |
| Vicat softening point (A120) | 80±2 |
| Heating Shrinkage ratio 105 ℃/10min | ≥-8.0 % (longitudinal) &≥-4.0 %(transverse) |
| Surface Dyne (dynes/cm) | ≥38 |
| Normal thickness in mm | 0.10-0.76 |
| Density (g/cm3) | 1.30 ±0.05 |
| Peel Strength (90°, 300mm/min) | ≥6.0 N/cm |
| Aging time (65℃ temp./95% humidity ) | ＞200 hours |
| Suitable ink | offset and silk screen printing UV ink, Pigment and dye ink for inkjet printing as well as digital printing ink |
3.PETG Plastic Sheet /PETG Card Core sheet for high-end credit cards and Smart cards Production- Application
Card-making method:
1). Print the patterns directly to the material
2). Laminate with overlay
3). Punching
4). Other art-work
| Product model | Product name | Thickness Range mm | Color | Vicat ℃ | dynes/cm | Apparent density g/cm3 | Peel strength N/cm | Main application |
| PETG | PETG core | 0.1-0.76 | White
| 78-80 | ≥38 | 1.3+/-0.05 | / | It is used for national ID cards and other high grade cards.It is capable of achieving laser ablation, sunken cord, leveling up, printed layer,and has resistance to high temperature, high strength and environmental protection. |
| Item | Unit | Value | |
| Density | g/cm3 | 1.30 ±0.05 | |
| Tensile Strength | Horizontal | MPa | ≥50 |
| Vertical | ≥50 | ||
| Vicat | ℃ | 78-80 | |
| Surface Dyne | dynes/cm | ≥38 | |
| Thickness range | mm | 0.1-0.76mm | |
4.PETG Plastic Sheet /PETG Card Core sheet for high-end credit cards and Smart cards Production- Packing